How structural flaws dictate failure strength and deformation in nanosized alloys
(Nanowerk News) A study from A*STAR reveals that designers of metallic-glass-based nanodevices must account for tiny flaws in alloy frameworks to avoid unpredictable catastrophic failure ("Mechanisms of Failure in Nanoscale Metallic Glass"). Understanding how nanoscale metallic glass fractures and fails when subjected to external stress is critical to improving its reliability in devices and composites.
Recently, researchers have found evidence that artificial flaws — miniscule notches carved into the alloy — do not affect the material’s overall tensile strength. But other work has shown that such notches may actually induce the formation of localized cracks.
Mehdi Jafary-Zadeh and co-workers from the A*STAR Institute of High Performance Computing, in collaboration with researchers in the United States, used a combination of physical experiments and computational simulations to study nanoscale flaw tolerance with in-depth precision. First, the researchers fabricated nickel–phosphorous metallic glass into narrow ‘nanopillars’ bearing tiny notches and mushroom-shaped endcaps that served as tension grips (see image). Guided by high-resolution scanning electron microscopy, they systematically pulled the structures apart until they cracked — an action that consistently occurred at the notched zone, and at failure strengths 40 per cent lower than those for unflawed nanopillars.
The team then turned to massive molecular dynamics simulations to explain these physical results. “Simulating failure modes in the nanopillar metallic glasses required large-scale, three-dimensional models containing millions of atoms,” says Jafary-Zadeh. “Performing simulations at these scales is pretty daunting, but we overcame this challenge with the help of the A*STAR Computational Resource Centre.”
When the researchers modeled atomic strain during nanopillar elongation, they found that the un-notched structures failed via a plastic type of deformation known as shear banding. However, the notched structures were brittle and failed through crack propagation from the flaw point at tensile strengths significantly smaller than the un-notched samples (see video). These observations suggest that ‘flaw insensitivity’ may not be a general feature of nanoscale mechanical systems.
A molecular dynamics simulation of failure in a notched metallic glass nanopillar due to crack propagation.
“The theory of flaw insensitivity postulates that the strength of materials that are intrinsically brittle or have limited plastic deformation modes approaches a theoretical limit at the nanoscale, and does not diminish due to structural flaws,” explains Jafary-Zadeh. “However, our results show that failure strength and deformation in amorphous nanosolids depend critically on the presence of flaws.”
Jafary-Zadeh notes that the excellent agreement between experimental results and the simulations is exciting and demonstrates how such computations can bridge the knowledge gap between macroscopic mechanical fracturing and the hidden corresponding mechanisms taking place at atomistic time and length scales.