New 3D-printed cement paste gets stronger when it cracks - just like structures in nature

(Nanowerk News) What if the inherent weaknesses of a material actually made houses and buildings stronger during wildfires and earthquakes?
Purdue University researchers have 3D-printed cement paste, a key ingredient of the concrete and mortar used to build various elements of infrastructure, that gets tougher under pressure like the shells of arthropods such as lobsters and beetles. The technique could eventually contribute to more resilient structures during natural disasters.
"Nature has to deal with weaknesses to survive, so we are using the 'built-in' weaknesses of cement-based materials to increase their toughness," said Jan Olek, a professor in Purdue's Lyles School of Civil Engineering.
The idea would be to use designs inspired by arthropod shells to control how damage spreads between the printed layers of a material, like trying to break a bunch of uncooked spaghetti noodles as opposed to a single noodle.
"The exoskeletons of arthropods have crack propagation and toughening mechanisms that we can reproduce in 3D-printed cement paste," said Pablo Zavattieri, Purdue professor of civil engineering.
3D-printed cement-based materials – such as cement paste, mortar and concrete – would give engineers more control over design and performance, but technicalities have stood in the way of scaling them up.
Purdue engineers are the first to use 3D printing to create bioinspired structures using cement paste, as shown in a published paper and the frontispiece for an upcoming print issue of the journal Advanced Materials ("Additive Manufacturing and Performance of Architectured Cement-Based Materials").
bioinspired 3D-printed cement paste
The first-ever bioinspired 3D-printed cement paste element shows promise for making infrastructure more resilient to mechanical loads, like those that occur during natural disasters. (Purdue University Concrete 3D Printing Team/Mohamadreza Moini)
"3D printing has removed the need for creating a mold for each type of design, so that we can achieve these unique properties of cement-based materials that were not possible before," said Jeffrey Youngblood, Purdue professor of materials engineering.
The team is also using micro-CT scans to better understand the behavior of hardened 3D-printed cement-based materials and take advantage of their weak characteristics, such as pore regions found at the "interfaces" between the printed layers, which promote cracking. This finding was recently presented at the 1st RILEM International Conference on Concrete and Digital Fabrication.
"3D printing cement-based materials provides control over their structure, which can lead to the creation of more damage and flaw-tolerant structural elements like beams or columns," said Mohamadreza "Reza" Moini, a Purdue Ph.D. candidate of civil engineering.
The team was initially inspired by the mantis shrimp, which conquers its prey with a "dactyl club" appendage that grows tougher on impact through twisting cracks that dissipate energy and prevent the club from falling apart.
Some of the bioinspired cement paste elements designed and fabricated by the team using 3D printing techniques include the "honeycomb," "compliant" and "Bouligand" designs, called "architectures."
Each of these architectures allowed for new behaviors in a 3D-printed element once hardened. The Bouligand architecture, for example, takes advantage of weak interfaces to make a material more crack-resistant, whereas the compliant architecture makes cement-based elements act like a spring, even though they are made of brittle material.
The team plans to explore other ways that cement-based elements could be designed for building more resilient structures.
Source: Purdue University